Inspectioneering

Embrittlement

Explore this topic

Redirected from Temper Embrittlement

Embrittlement is the process of a material becoming brittle due to a loss of ductility. Hydrogen embrittlement, temper embrittlement, liquid metal embrittlement, and sulfide stress cracking (SSC) are all examples of embrittlement. Embrittlement can be a very dangerous mechanism, leaving it unchecked can lead to cracking or even catastrophic brittle failure.

While each of the above mentioned mechanisms are similar in that the symptom of the mechanism is loss of ductility (embrittlement), each can have very different causes.

Hydrogen embrittlement occurs when atomic hydrogen diffuses into certain metals and those metals are put under applied tensile stresses, it can affect metals under both high and low temperature conditions. This type of embrittlement can affect materials during any number of operations such as welding, applying cathodic protection, pickling, phosphating, electroplating, forming, or finishing operations.

Temper embrittlement is caused by the presence of impurities of certain elements in the steel, such as antimony, phosphorous, tin, or arsenic when heating the metal from either 250 to 400 °C or from 450 to 650 °C. Unlike many other types of embrittlement, temper embrittlement can sometimes be reversible.

Liquid metal embrittlement is a type of embrittlement that can occur when molten metals come in contact with certain materials. This type of embrittlement is particularly dangerous because cracking rates from this mechanism can be exceedingly rapid and failure can occur within seconds.

Sulfide Stress Cracking (SSC) can occur at locations where atomic hydrogen is able to diffuse at sites of high internal stress, such as grain boundaries, inclusions and regions of triaxial stress at notches. When placed in proximity to tensile stresses this can lead to embrittlement.

Because of all this, it’s important that any operators be aware of any causes of embrittlement that can affect their in service equipment. Embrittlement is an insidious condition, but with awareness and preparation it can be prevented.

Related Topics

Relevant Links

Topic Tools

Share this Topic

Contribute to Definition

We welcome updates to this Integripedia definition from the Inspectioneering community. Click the link below to submit any recommended changes for Inspectioneering's team of editors to review.

Contribute to Definition
Articles about Embrittlement
November/December 2023 Inspectioneering Journal

Part 2 of this three-part series on brittle fracture focuses on methods for evaluating the risk in pressure equipment and the evolution of screening and assessment methods.

September/October 2023 Inspectioneering Journal

This article is Part 1 of a new three-part series on brittle fracture and focuses on the fundamental concepts and damage morphology associated with the unstable rupture of pressure equipment.

May/June 2020 Inspectioneering Journal

There are many places where brittle fracture risk can sneak into your plant and many reasons why a new or revised brittle fracture assessment may be required when reviewing your pressure systems. Don’t overlook this dangerous failure mechanism.

Authors: Greg Garic
September/October 2005 Inspectioneering Journal

Temper embrittlement is another form of metallurgical degradation resulting from exposure of susceptible low alloy steels to higher temperature ranges, usually in service, but can occur to some extent even during heat treatment. And, once again, if...

Authors: John Reynolds
September/October 2005 Inspectioneering Journal

Another form of metallurgical degradation at higher temperatures is called sigma phase embrittlement. As the name implies, a metallurgical phase change occurs in some stainless steels when they are heated above about 1000F (540C).

Authors: John Reynolds
Partner Content

Pinnacle's data-driven reliability framework ensures the right data is fueling the right intelligence, helping you make confident, strategic decisions.

September/October 2005 Inspectioneering Journal

Titanium (Ti) hydriding is another somewhat unusual metallurgical degradation phenomena that can result in brittle fracture. Unlike many other steel embrittlement phenomena, this one most often occurs in thin wall Ti tubes that have been selected...

Authors: John Reynolds
July/August 2003 Inspectioneering Journal

This is the name given to a form of embrittlement that occurs in 400 series of stainless steels, duplex SS's and less commonly in some 300 series stainless steels containing a metallurgical phase called ferrite. The embrittlement occurs from 600...

Authors: John Reynolds
    Companies
    Downloads & Resources related to Embrittlement
      Asset Intelligence Report

      This Asset Intelligence Report on the hydrogen bake-out process serves as a primer to increase your familiarity with this technique used to drive hydrogen out of equipment prior to welding.

      eBook

      This publication outlines 101 Essential Elements that need to be in place and functioning well in order to effectively and efficiently preserve and protect the reliability and integrity of pressure equipment (i.e. vessels, exchangers, furnaces,...


      Inspectioneering Journal

      Explore over 20 years of articles written by our team of subject matter experts.

      Company Directory

      Find relevant products, services, and technologies.

      Training Solutions

      Improve your skills in key mechanical integrity subjects.

      Case Studies

      Learn from the experience of others in the industry.

      Integripedia

      Inspectioneering's index of mechanical integrity topics – built by you.

      Industry News

      Stay up-to-date with the latest inspection and asset integrity management news.

      Blog

      Read short articles and insights authored by industry experts.

      Expert Interviews

      Inspectioneering's archive of interviews with industry subject matter experts.

      Event Calendar

      Find upcoming conferences, training sessions, online events, and more.

      Downloads

      Downloadable eBooks, Asset Intelligence Reports, checklists, white papers, and more.

      Videos & Webinars

      Watch educational and informative videos directly related to your profession.

      Acronyms

      Commonly used asset integrity management and inspection acronyms.